文献类型：期刊文章

作　　者：周世博[1,2] 刘婷婷[3] 汤爱涛[1,4] 时慧[2] 敬学锐[1] 彭鹏[5] 章建跃[6] 潘复生[1,4]

Shi-bo ZHOU;Ting-ting LIU;Ai-tao TANG;Hui SHI;Xue-rui JING;Peng PENG;Jian-yue ZHANG;Fu-sheng PAN(College of Materials Science and Engineering,Chongqing University,Chongqing 400044,China;Institute of Metallic Biomaterials,Helmholtz-Zentrum Hereon,Max-Planck-Straße 1,D-21502,Geesthacht,Germany;School of Materials and Energy,Southwest University,Chongqing 400715,China;National Engineering Research Center for Magnesium Alloys,Chongqing University,Chongqing 400044,China;School of Metallurgy and Materials Engineering,Chongqing University of Science and Technology,Chongqing 401331,China;Department of Materials Science and Engineering,The Ohio State University,Columbus,OH 43210,USA)

机构地区：[1]重庆大学材料科学与工程学院,重庆400044 [2]Institute of Metallic Biomaterials,Helmholtz-Zentrum Hereon,Max-Planck-Straße 1,D-21502,Geesthacht,Germany [3]西南大学材料与能源学院,重庆400715 [4]重庆大学镁合金国家工程研究中心,重庆400044 [5]重庆科技学院冶金和材料工程学院,重庆401331 [6]Department of Materials Science and Engineering,The Ohio State University,Columbus,OH 43210,USA

出　　处：《Transactions of Nonferrous Metals Society of China》

基　　金：funded by the National Natural Science Foundation of China (Nos. 02110023210043, 51971042, U2167213, 51901028);supported by Sinoma Institute of Materials Research (Guang ZHOU) Co., Ltd (SIMR);gratefully acknowledged for financial support for Shi-bo ZHOU (No. 202106050089)

年　　份：2024

卷　　号：34

期　　号：2

起止页码：504-518

语　　种：中文

收录情况：AJ、CAS、CSCD、CSCD2023_2024、EAPJ、EBSCO、EI、INSPEC、JST、SCIE、SCOPUS、WOS、ZGKJHX、普通刊

摘　　要：分析微量锰添加对镁合金显微组织和力学性能的影响。采用电子背散射技术、迹线分析、透射电镜和粘塑性自洽模拟等方法研究变形过程中的塑性变形机理。结果表明:Mn的加入使Mg−Mn合金的平均晶粒尺寸由28.30μm减小到5.10μm;同时,随着Mn含量的增加,样品的断裂伸长率由14.33%提高到20.33%,屈服强度则由84 MPa提高到180 MPa。这种同时提高塑性和强度的原因是基面滑移和非基面滑移之间的临界剪切应力差从173 MPa减小到115 MPa,导致非基面滑移活动明显增加。通过微合金元素调整滑移系统差异为开发具有高强度和延展性的镁合金提供了一种途径。

关 键 词：镁合金 显微组织演变 力学性能 塑性 变形机理  

分 类 号：TG146.22[材料类]