文献类型：期刊文章

作　　者：刘志浩[1,2] 韩鹏[1] 王文[1] 关肖虎[1] 王智[1] 方园[1] 乔柯[1] 叶东明[1] 蔡军[1] 谢迎春[2] 王快社[1]

Zhi-hao LIU;Peng HAN;Wen WANG;Xiao-hu GUAN;Zhi WANG;Yuan FANG;Ke QIAO;Dong-ming YE;Jun CAI;Ying-chun XIE;Kuai-she WANG(National and Local Joint Engineering Research Center for Functional Materials Processing,School of Metallurgical Engineering,Xi’an University of Architecture and Technology,Xi’an 710055,China;Guangdong Provincial Key Laboratory of Modern Surface Engineering Technology,National Engineering Laboratory of Modern Materials Surface Engineering Technology,Institute of New Materials,Guangdong Academy of Sciences,Guangzhou 510651,China)

机构地区：[1]西安建筑科技大学冶金工程学院功能材料加工国家地方联合工程研究中心,西安710055 [2]广东省科学院新材料研究所现代表面工程技术国家工程实验室,广东省现代表面工程技术重点实验室,广州510651

出　　处：《Transactions of Nonferrous Metals Society of China》

基　　金：supports from the National Natural Science Foundation of China(Nos.51974220,52001078,52104383,52034005);the National Key Research and Development Program of China(No.2021YFB3700902);the Shaanxi Provincial National Science Fund for Distinguished Young Scholars,China(No.2022JC-24);the Guangdong Basic and Applied Basic Research Foundation,China(No.2019B1515120016).

年　　份：2023

卷　　号：33

期　　号：11

起止页码：3250-3265

语　　种：中文

收录情况：AJ、CAS、CSCD、CSCD2023_2024、EAPJ、EBSCO、EI、IC、JST、SCIE、SCOPUS、WOS、ZGKJHX、普通刊

摘　　要：采用冷喷摩擦复合增材制造(CFAM)技术制备6061铝合金块体材料。采用OM、SEM和EBSD对冷喷涂(CS)和CFAM试样的显微组织进行表征,通过显微硬度、拉伸和腐蚀实验研究两者的力学性能和腐蚀行为。结果表明,与CS试样相比,CFAM试样的显微组织更加致密和均匀,晶粒细小等轴,平均晶粒尺寸为3.1μm,显微硬度、极限抗拉强度和伸长率分别提高了22%、171%和683%。CFAM试样的腐蚀电流密度比CS试样低95.1%~97.8%,腐蚀机理由CS试样的点腐蚀转变为晶间腐蚀。

关 键 词：冷喷摩擦复合增材制造  6061铝合金 显微组织 力学性能 腐蚀机理  

分 类 号：TG146.21[材料类] TG172]