文献类型：期刊文章

作　　者：汪雨微[1] 欧宝立[1,2,3,4,5] 鲁忆[1] 邢赟[1] 罗子盈[1] 支倩[1] 曹新秀[1]

Yuwei WANG;Baoli OU;Yi LU;Yun XING;Ziying LUO;Qian ZHI;Xinxiu CAO(School of Materials Science and Engineering,Hunan University of Science and Technology,Xiangtan 411201,China;State Key Laboratory of Tribology,Tsinghua University,Beijing 100084,China;Hunan Provincial Key Defense Laboratory of High Temperature Wear-Resisting Materials and Preparation Technology(Hunan University of Science and Technology),Xiangtan 411201,China;Hunan Provincial Key Lab of Advanced Materials for New Energy Storage and Conversion(Hunan University of Science and Technology),Xiangtan 411201,China;Hunan Provincial Key Laboratory of Controllable Preparation and Functional Application of Fine Polymers(Hunan University of Science and Technology),Xiangtan 411201,China)

机构地区：[1]湖南科技大学材料科学与工程学院,湘潭411201 [2]清华大学摩擦学国家重点实验室,北京100084 [3]高温耐磨材料及制备技术湖南省国防科技重点实验室(湖南科技大学),湘潭411201 [4]新能源储存与转换先进材料湖南省重点实验室(湖南科技大学),湘潭411201 [5]精细聚合物可控制备及功能应用湖南省重点实验室(湖南科技大学),湘潭411201

出　　处：《复合材料学报》

基　　金：国家自然科学基金面上项目(51775183);湖南省自然科学基金项目(2021JJ30259);清华大学摩擦学国家重点实验室开放基金项目(SKLTKF17B14);国家级大学生创新创业项目(S202010534001S);湖南省普通高等学校教学改革研究项目(湘教通[2019]291号);湖南省大学生创新创业项目(S202010534033)。

年　　份：2021

卷　　号：38

期　　号：12

起止页码：3971-3985

语　　种：中文

收录情况：AJ、BDHX、BDHX2020、CAS、CSCD、CSCD2021_2022、EAPJ、EI、IC、JST、RCCSE、SCOPUS、ZGKJHX、核心刊

摘　　要：超疏水材料在金属防腐领域具备巨大的潜在应用前景。为得到疏水性能及防腐性能俱优的纳米TiO_(2)/环氧树脂复合涂层材料,首先以三甲氧基十七氟癸基硅烷和γ-氨丙基三乙氧基硅烷(KH550)对纳米TiO_(2)表面功能化;以全氟辛基甲基丙烯酸酯对固化剂二乙烯三氨(DETA)进行氟化;最后通过一步共混法和两步喷涂法分别制备出两种复合涂层。利用FTIR、XPS、^(1)HNMR分析氟化固化剂(F-DETA)和氟化纳米TiO_(2)(f-TiO_(2))的物相组成和组织结构。接触角测试仪和静置实验表明,当三甲氧基十七氟癸基硅烷和γ-氨丙基三乙氧基硅烷的摩尔比为1∶15时f-TiO_(2)的性能最佳,所制备的复合涂层接触角达到164.9°。SEM表征结果显示通过两步法制备的f-TiO_(2)/环氧树脂复合涂层具备更均匀的粗糙表面、涂层内部孔隙率较低且环氧树脂层与f-TiO_(2)层具备梯度结构。摩擦实验证明两步法制备的f-TiO_(2)/环氧树脂复合涂层的超疏水性具备较好的机械稳定性。Tafel极化曲线和电化学阻抗谱(EIS)研究表明,通过两步法制备的f-TiO_(2)/环氧树脂复合涂层具有优异的防腐性能,其腐蚀抑制效率高达99.99%。

关 键 词：纳米TiO_(2)  环氧树脂 超疏水 防腐蚀 复合涂层  