文献类型：期刊文章

作　　者：徐家跃[1] 梁肖肖[1] 金敏[2] 曾海波[1,3] KIMURA Hideo[4] 胡皓阳[2] 邵和助[2] 申慧[1] 田甜[1] 李海霞[1]

XU Jia-Yue;LIANG Xiao-Xiao;JIN Min;ZENG Hai-Bo;KIMURA Hideo;HU Hao-Yang;SHAO He-Zhu;SHEN Hui;TIAN Tian;LI Hai-Xia(Institute of Crystal Growth,School of Materials Science and Engineering,Shanghai Institute of Technology,Shanghai 201418,China;College of Materials,Shanghai Dianji University,Shanghai 201306,China;Institute of Optoelectronics and Nanomaterials,College of Materials Science and Engineering,Nanjing University of Science and Technology,Nanjing 210094,China;National Institute for Materials Science,1-2-1 Sengen,Tsukuba,Ibaraki 305-0047,Japan)

机构地区：[1]上海应用技术大学材料科学与工程学院晶体生长研究所,上海201418 [2]上海电机学院材料学院,上海201306 [3]南京理工大学材料科学与工程学院纳米光电材料研究所,南京210094 [4]National Institute for Materials Science,1-2-1 Sengen,Tsukuba,Ibaraki 305-0047,Japan

出　　处：《无机材料学报》

基　　金：National Natural Science Foundation of China(51472263,51572175,61605116);Ningbo Natural Science Foundation(2017A610009);Public Projects of Zhejiang Province(2017C31006);Shanghai Natural Science Foundation(15ZR1440600)

年　　份：2018

卷　　号：33

期　　号：11

起止页码：1253-1258

语　　种：中文

收录情况：BDHX、BDHX2017、CAS、CSA、CSA-PROQEUST、CSCD、CSCD2017_2018、EI、IC、JST、RCCSE、SCIE、SCOPUS、WOS、ZGKJHX、核心刊

摘　　要：利用自制移动区熔炉生长了CsPbBr_3晶体,事先采用相同工艺合成了高纯多晶原料以去除杂质和水分。通过工艺优化获得了大尺寸CsPbBr_3晶体,达到Ф25 mm×60 mm。该晶体呈橘红色,在600～2000 nm波长范围内具有透过率达78.6%的优异透光性能。热分析表明,所得CsPbBr_3晶体在88.1℃和131.25℃时存在正交-四方和四方-立方相变。计算得到CsPbBr_3晶体的带宽E_g=2.25eV。上述结果表明移动区熔法是一种具有应用潜力的制备高质量大尺寸CsPbBr_3晶体的生长方法。

关 键 词：移动区熔法  CsPbBr3晶体  透过率 带隙

分 类 号：TQ174]