文献类型：期刊文章

作　　者：戴甲洪[1] 谢红梅[1] 蒋斌[2,3] 彭程[1] 姜中涛[4] 杨青山[5] 潘复生[2,3]

Dai Jiahong;Xie Hongmei;Jiang Bin;Peng Cheng;Jiang Zhongtao;Yang Qingshan;Pan Fusheng(Yangtze Normal University,Chongqing 408100,China;State Key Laboratory of Mechanical Transmissions,Chongqing University,Chongqing 400044,China;Chongqing Academy of Science and Technology,Chongqing 401123,China;Chongqing University of Arts and Sciences,Chongqing 402160,China;Chongqing University of Science and Technology,Chongqing 401331,China)

机构地区：[1]长江师范学院,重庆408100 [2]重庆大学机械传动国家重点实验室,重庆400044 [3]重庆科学技术研究院,重庆401123 [4]重庆文理学院,重庆402160 [5]重庆科技学院,重庆401331

出　　处：《稀有金属材料与工程》

基　　金：Chongqing Science and Technology Commission(2014jcyjjq0041,2015zdcy-ztzx50003);National Natural Science Foundation of China(51531002,51474043);National Key Research and Development Program of China(2016YFB0301104);Education Commission of Chongqing Municipality(KJZH14101,KJ1601302);Fundamental Research Funds the Central Universities(CK2016B18);Fundamental Research Funds for the Yangtze Normal University(2016KYQD15,2016XJQN32)

年　　份：2018

卷　　号：47

期　　号：7

起止页码：2042-2048

语　　种：中文

收录情况：AJ、BDHX、BDHX2017、CAS、CSA-PROQEUST、CSCD、CSCD2017_2018、EI、IC、INSPEC、JST、RCCSE、SCIE、SCOPUS、WOS、ZGKJHX、核心刊

摘　　要：研究了Mg-40Al与Mg-20Ce固液界面在475、500和525℃下保温5～30 min的界面反应和扩散层的生长动力学。结果发现,在扩散层中由于Al元素和Ce元素反应生成Al_(11)Ce3、Al_3Ce和Al_2Ce金属化合物。金属化合物的体积分数随着扩散温度的升高而增加。扩散层的生长满足抛物线生长规律,扩散层的扩散激活能为(42±3.7)kJ/mol。实验研究的固液扩散为理解合金熔炼过程中金属化合物的形成提供了理论基础。

关 键 词：镁 扩散 界面  金属合金物  动力学

分 类 号：TG146.22[材料类]