文献类型：期刊文章

作　　者：黄绘敏[1] 李振宇[1] 杨帆[1] 王威[1] 王策[1]

机构地区：[1]吉林大学麦克德尔米德实验室,长春130012

出　　处：《高等学校化学学报》

基　　金：国家自然科学基金(批准号:50473008和50673034)资助

年　　份：2007

卷　　号：28

期　　号：6

起止页码：1200-1202

语　　种：中文

收录情况：AJ、BDHX、BDHX2004、CAS、CSCD、CSCD2011_2012、EI(收录号：20073210755443)、IC、JST、RCCSE、RSC、SCIE、SCOPUS、WOS、ZGKJHX、核心刊

摘　　要：Ultrafine polystyrene(PS) nanofibers were prepared via the simple electrospinning technique.Uniform and smooth PS nanofibers were obtained with adding the organic salt BTEAC into the PS solutions and adjusting the concentration of PS solutions.Without the addition of BTEAC,PS fibers with few beads could be achieved with a PS mass fraction of 20%,and the average diameter of the fibers was 280 nm.The addition of the organic salt BTEAC could lower the critical concentration for the fiber formation and reduce the amount of beads on the fibers.Unltrafine PS fibers without any beads were obtained with a PS mass fraction of 10% and an ionic salt mass fraction of 0.5%.The average diameter of the fiber was successfully reduced to 100 nm.The influence of the salt concentration on the morphology and diameter of the PS fibers was also investigated.The viscosity and surface tension changes were measured with changing the concentration of BTEAC.The results show that the changes were so small that these factors could be ignored.It was suggested that variations of the fiber diameter should be mainly resulted from the changes of conductivity and conformation of the polymer chain as the concentration of BTEAC is varied.

关 键 词：静电纺丝 聚苯乙烯 纳米纤维

分 类 号：O631]